Volatile Matter,% ≤

0.75

-

-

0.75

0.65

Total Ash,% ≤

0.3

-

-

0.3

0.3

Raw Rubber Mooney Viscosity

ML1001+4C

45

45±4

44±5

45

45

Compound Mooney Viscosity

ML1001+4℃ ≤

68

-

-

68

65

300% Tensile Stress MPa

25min

8.5

8, 8

8, 8

8.5

8.5

35min

9

-

-

9

9

50min

8.8

-

-

8.8

8.7

Tensile Strength MPa35min ≥

14.2

11, 0

16,8

14.2

14.3

Elongation, % 35min ≥

450

360

360

450

420

Features

High elasticity, low hysteresis loss and heat generation, low temperature filling and good fluidity in the film, excellent wear resistance and flex resistance.

have good

abrasion resistance and

Flex resistance

sex, flexibility

high resistance

temperature.

have good

abrasion resistance and

Flex resistance

sex, flexibility

high resistance

temperature.

There are disadvantages such as poor processing performance and the tendency of constant cold flow in raw rubber. The emergence of oil-extended butadiene rubber can improve the above shortcomings to a certain extent.

It has the characteristics of high elasticity, good wear resistance, good cold resistance, low heat generation, good flexibility and dynamic performance.

Product Usage

In the manufacture of tires, hoses, tapes, seals, soles and other rubber products.

Used to make tire treads, conveyor belts, shoe soles, insulated cables.

Used to make tire treads, conveyor belts, shoe soles, insulated cables.

For the preparation of tires, hoses, rubber sheets, for the preparation of water-soluble anodic electrophoretic paints, adhesives, thermosetting resins, and for rubber and plastic modification, and also for the manufacture of hoses, tapes, tires, seals, shoe soles and cables and other rubber products.

Mainly used for tires, shoes,

high impact polystyrene and

Modification of ABS resin, etc.